CuxZn1-xO thin films were prepared by the sol-gel process. Microstructure, surface topography and optical properties were studied by X-ray diffractometry, atom force microscopy, UV-Vis spectrophotometer and fluorescence spectrometer. The monoclinic CuO phase has been observed in CuxZn1-xO (x = 0.05, 0.10, and 0.15) thin films annealed at 800 degrees C. Preferential c-axis orientation of the CuxZn1-xO thin films annealed at 800 degrees C increases with the increase of x value. The annealing temperature and CuO component have great effect on the absorption coefficient of CuxZn1-xO thin films in the visible region. The decrease of optical band gap may be attributed to the reduction of the fraction of the amorphous phase and stoichiometry deficiency of ZnO due to CuO doping. The deep level emission in ZnO thin film originates from oxygen vacancy and oxygen interstitial defects. The violet emission peaked at about 400 nm has been assigned to the electron transition from zinc interstitial level and the valence band.
Jianguo Lv,Zhitao Zhou,Feng Wang,Changlong Liu,Wanbing Gong,Jielin Dai,Xiaoshuang Chen,Gang He,Shiwei Shi,Xueping Song,Zhaoqi Sun,Feng Liu.
Superlattices and Microstructures,61,115-123(2013)